Several full-scale rigid pavement slabs were constructed and tested under constant cyclic loading for fatigue. To provide the comparable maximum applied stress to number of cycles to failure (S-N) relationships for the full-scale field slabs, laboratory beam fatigue testing was conducted before field testing with the use of the same concrete mix designs. The superaccelerated pavement testing technique that was developed at the University of Texas was used in the field. The stationary dynamic deflectometer (SDD) was used to load the full-scale concrete slabs. To monitor the response of the rigid pavements, accelerometers and linear variable differential transformers were installed, and dynamic and permanent displacements of slabs were recorded during the entire testing period. All test slabs reached fatigue failure under the interior loading configuration using the SDD. This field loading system was found to be a practical and effective tool for testing the full-scale rigid pavement system. During fatigue loading, cracks began at the bottom of the slabs at the loading locations and propagated along the bottom of the slab centerline, which was the maximum stress path. Vertical crack propagation at the edge and stress redistribution occurred for the part of the slab’s fatigue life. The concept of equivalent fatigue life was applied to correct the effect of the different stress ratios between the field and the laboratory testing. The laboratory beams and full-scale field slabs showed an almost identical S-N relationship after the correction for the variance of stress ratio.

01023790

English

pp 113-124

2005

Transportation Research Record: Journal of the Transportation Research Board

0309094151

Print

Figures (6) ; Photos (10) ; References (12) ; Tables (4)

Failure; Fatigue (Mechanics); Field tests; Rigid pavements; Slabs; Stress ratio

Accelerated pavement tests; Crack propagation; Displacements; Dynamic displacements; Fatigue life; Stationary dynamic deflectometers; Superaccelerated pavement testing

Design; Highways; Pavements; I22: Design of Pavements, Railways and Guideways; I23: Properties of Road Surfaces

TRIS, TRB, ATRI

May 7 2006 5:55PM

• Accuracy of Ground-Penetrating Radar for Estimating Rigid and Flexible Pavement Layer Thicknesses
• Analysis of Long-Term Effectiveness of Thin Hot-Mix Asphaltic Concrete Overlay Treatments
• Assessment of Aging at FHWA’s Pavement Testing Facility
• Developing Roadway Standards for Ride Quality from the Customer’s Perspective
• Development of a Crack Type Index
• Evaluation of Top-Down Cracks in Asphalt Pavements by Using a Self-Calibrating Ultrasonic Technique
• Incorporating Variability into Pavement Performance, Life-Cycle Cost Analysis, and Performance-Based Specification Pay Factors
• Pavement Management System Based on Financial Consequence
• Prediction of Pavement Crack Initiation from In-Service Pavements: A Duration Model Approach
• Quantification of Pavement Damage Caused by Dual and Wide-Base Tires
• Rut Initiation Mechanisms in Asphalt Mixtures as Generated Under Accelerated Pavement Testing
• Statistical Analysis of Automated Versus Manual Pavement Condition Surveys
• Use of Pavement Management System Data to Monitor Performance of Pavements Under Warranty
• Wavelet-Based Multiresolution Analysis of Pavement Profiles as a Diagnostic Tool
• Wavelet-Based Pavement Distress Classification