Calcium hydroxide [Ca(OH)2] is one of the major constituents of hydrated portland cement paste. Its content can be used to trace the progress of cement hydration or serve as an indicator of the extent of pozzolanic reaction. The thermogravimetric analysis (TGA) method is often used to determine the Ca(OH)2 content because it is a relatively easy and fast procedure. However, no universally accepted method exists for the preparation of TGA specimens and for the interpretation of the resulting TGA curves. This paper presents an investigation on the contents of Ca(OH)2 in samples subjected to different preparation techniques. The results showed that a certain amount of calcium carbonate (CaCO3) was produced as a result of carbonation during the sample preparation process. The degree of carbonation was dependent on the sample preparation, and carbonated Ca(OH)2 was considered to determine the accurate total Ca(OH)2 content. In addition, a modified interpretation of the TGA curve for Ca(OH)2 was suggested. In this interpretation, the mass losses caused by the other hydration products, except for the Ca(OH)2 and the carbonated Ca(OH)2, were considered so that the accurate content of Ca(OH)2 could be determined. The interpretation technique was verified by comparing the results with those obtained by differential scanning calorimetry. Ultimately, the actual contents of Ca(OH)2 in pastes undergoing different sample preparation techniques were determined by using the modified interpretation of the TGA curve for the Ca(OH)2. The results showed that this interpretation yielded comparable contents of Ca(OH)2 in most of the sample preparation techniques used in this study.

01455586

12-4378

English

pp 10–18

2012

Transportation Research Record: Journal of the Transportation Research Board

9780309223300

Print

Figures; References; Tables

Calcium carbonate; Calcium hydroxide; Cement paste; Hydration; Mortar; Pozzolanic action; Thermogravimetric analysis

Sample preparation

Highways; Materials; I32: Concrete

TRIS, TRB, ATRI

Feb 8 2012 5:23PM

• Can Soy Methyl Esters Improve Concrete Pavement Joint Durability?
• Development of Laboratory Testing Protocol for Rapid-Setting Cementitious Material for Airfield Pavement Repairs
• Development of Photocatalytic Pervious Concrete Pavement for Air and Storm Water Improvements
• Development of Precision Statement for Concrete Surface Resistivity
• Drying Shrinkage Behavior of Mortars Made with Ternary Blends
• Durability of Pavement Concretes Made with Recycled Concrete Aggregates
• Effect of Recycled Concrete Aggregate Properties on Mixture Proportions of Structural Concrete
• Effects of Deicing Salt Solutions on Physical Properties of Pavement Concretes
• Field Evaluation of Ability of Photocatalytic Concrete Pavements to Remove Nitrogen Oxides
• Fingerprinting of Chemical Admixtures in Fresh Portland Cement Concrete by Portable Infrared Spectrometer
• Freeze–Thaw Durability and Salt Scaling Resistance Assessment of Portland Cement Concrete Composite Pavement
• Lowering the Carbon Footprint of Concrete by Reducing Clinker Content of Cement
• Performance of Concrete Incorporating Stone Industry Waste as Aggregates
• Performance of Slag Cement in Hydraulic Cement Concrete
• Predicting Cement–Admixture Incompatibilities with Cement Paste Rheology
• Quantification of Reduction of Nitrogen Oxides by Nitrate Accumulation on Titanium Dioxide Photocatalytic Concrete Pavement
• Reducing Curing Requirements for Pervious Concrete with a Superabsorbent Polymer for Internal Curing
• Reducing Set Retardation in High-Volume Fly Ash Mixtures with the Use of Limestone: Improving Constructability for Sustainability
• Strength and Transport Properties of Concretes Modified with Coarse Limestone Powder to Compensate for Dilution Effects
• Surface Resistivity Measurements Evaluated as Alternative to Rapid Chloride Permeability Test for Quality Assurance and Acceptance